Ki jan pousantaj refwadisman tretman chalè soude apre -de 400 degre a 200 degre afekte detant estrès rezidyèl ak rezistans twou nan bouchon fen aparèy chofaj asye pur 316

Teknik soude nan bouchon fen kreye tansyon rès nan 316 Nerjaveèi asye ki vlope tib chofaj elektrik ki ka lakòz estrès korozyon krak (SCC) ak afekte rezistans pitting nan kondisyon klori. Estrès rezidyèl sa yo souvan elimine pa tretman chalè apre -soude (PWHT) nan 400-450 degre pou 1-2 èdtan. Sepandan, to a refwadisman soti nan tanperati PWHT a desann nan 200 degre gen yon efè konsiderab men jeneralman neglije sou tou de degre nan detant estrès ak rezistans nan korozyon nan materyèl la. Estanda 316 pral presipite carbure ki rich nan Kwòm nan limit grenn yo (sansiblite) si li refwadi dousman atravè ranje 300-450 degre. Refwadisman rapid (lè oswa dlo) kenbe estrikti a soulaje estrès san sansibilizasyon. Se lyen ki genyen ant pousantaj refwadisman PWHT, rediksyon estrès rezidyèl, ak rezistans pitting nan atik sa a, ki ofri yon fondasyon spesifikasyon pou optimize tretman apre soude.

Kontre efè soulajman estrès ak sansibilizasyon

De reyaksyon tèmik aktive fèt an menm tan pandan PWHT nan 400-450 degre nan 316 asye pur. Premye a se soulajman estrès. Estrès rezidyèl akòz soude (anjeneral 100-300 MPa) yo rilaks atravè mouvman debwatman ak rekiperasyon. Pwosesis la se logaritmik epi 70-80% estrès rezidyèl la lage apre 1 èdtan nan 450 degre. Dezyèm faz la se presipitasyon carbure: pi wo a tanperati apeprè 450 degre, carbure chromium ka nuklee, byenke presipitasyon se paresseux. Kòm materyèl la refwadi soti nan tanperati a PWHT li ankò ale nan seri a sansibilizasyon (450-850 degre). Sepandan, paske tanperati PWHT a (400-450 degre) pi ba pase ranje sansibilizasyon, pa gen okenn carbure adisyonèl presipite pandan kenbe a. Risk la rive lè gwo fou a refwadi dousman ak tanperati materyèl la ogmante pi wo pase 450 degre pandan refwadisman? Li pa fè sa - PWHT se te pote soti nan 400-450 degre Se poutèt sa refwadisman an ap kòmanse anba a ranje sansibilizasyon. Risk reyèl la se pou PWHT nan 500-600 degre (itilize pafwa pou plis lage estrès) lè refwadisman gradyèl nan 450-850 degre pwodui sansibilizasyon. Pandan PWHT 400-450 degre, enkyetid prensipal la se pa sansibilizasyon, men re-entwodiksyon nan estrès rezidyèl akòz refwadisman diferans. Nenpòt refwadisman ki pa inifòm (yon bò nan soude a refwadi pi vit pase lòt la) ta ka jenere nouvo estrès tèmik nan 50-100 MPa ki lajman anile avantaj ki genyen nan kenbe soulaje estrès la.

Quantification de enfliyans refwadisman yo ki te konn sou pitting rezistans ak rès tèt chaje

Finalman estrès rezidyèl te evalye pa X-difraksyon reyon ak pitting rezistans te evalye pa kritik pitting tanperati (CPT) tès nan 1 M NaCl, sou yon seri de pousantaj refwadisman soti nan yon 450 degre, 1-èdtan PWHT soude 316 bouchon (1.5 mm epesè miray) nan kontwole tès. Rezilta yo revele ke vitès la refwadisman gen yon efè minè sou sansibilizasyon (tout espesimèn yo te rete san sansiblite kòm tanperati a maksimòm pa janm travèse seri a sansibilizasyon) men yon efè fò sou estrès final la rezidyèl akòz efè gradyan tèmik.

Metòd refwadisman PWHT soti nan 450 degre Estimasyon to refwadisman (450 degre a 200 degre) Estrès rezidyèl final nan soude (MPa) Efikasite soulajman estrès (% nan kòm-estrès soude) Tanperati Kritik Pitting (degre) (1 M NaCl) Sèvis Rekòmande
Refwadisman founo (pouvwa koupe) 5-10 degre / èdtan 60-80 60-70 % 52-56 Non (pa efikas)
Toujou frèt lè (orizontal) 100-200 degre / èdtan 40-60 70-80 % 54-58 Apwopriye pou klori modere
Fanatik lè fòse 300-500 degre / èdtan 30-45 80-85 % 55-59 Wi
Dlo pasè (immersion) 1000-2000 degre / èdtan 20-30 85-90% 56-60Wi, pi bon klori segondè
Pa gen PWHT (tankou-soude) N/A 150-250 0 % 50-54 Pa pou sèvis klori
Ka espesyal PWHT nan 500-600 degre

In some situations where more comprehensive stress relief is required (e.g. heaters for high pressure duty or severe thermal cycling), PWHT at 500-600 °C for 1-2 hours is occasionally specified. Stress reduction efficiency at these temperatures is 90-95 % however the material is passed through the sensitisation range during heating and cooling. Severe sensitisation is seen in standard 316 (max 0.08 % C) with CPT decreasing to 35-40 °C and slow cooling from 550 °C, inappropriate for any chloride service. For these PWHT temperatures, the cooling rate is crucial. Water quenching from 550 °C (cooling rate >1000 degre / èdtan jiska 850 -450 degre) siprime sansibilizasyon nan tib ki gen miray mens, kenbe CPT a alantou 55-60 degre. Chòk tèmik soti nan dlo trempe yon pati soude, sepandan, ka pwovoke deformation oswa kraze. Solisyon pi pito pou nenpòt aparèy chofaj ki mande PWHT pi wo pase 480 degre se itilize 316L (maksimòm 0.03% C) . 316L se sibstansyèlman mwens sansib a sansibilizasyon epi li gen apèn presipitasyon carbure menm lè refwadi tou dousman soti nan 550 degre.

Rekòmandasyon pratik pou refwadisman PWHT

Pou pi fò nan 316 aparèy chofaj kouvri nan sèvis akeuz, PWHT sijere a se 450 degre pou 1 èdtan ki te swiv pa refwadisman lè fòse (pousantaj refwadisman 300-500 degre / èdtan). Tretman sa a diminye estrès rezidyèl yo pa 80-85% epi li pa pwodui sansibilizasyon, paske tanperati maksimòm lan rive pi ba pase ranje sansibilizasyon an. Trempe dlo ofri yon ti jan pi gwo rediksyon estrès men gen plis chans pou defòme epi li raman esansyèl. Tablo ki anba a sèvi kòm yon gid desizyon pou seleksyon tanperati PWHT, to refwadisman ak klas materyèl depann sou korozivite sèvis la.

Anviwònman sèvis Nivo klori (ppm) Tanperati maksimòm ( degre ) Rekòmande PWHT Pousantaj refwadisman Klas materyèl
Sèk (ki pa-klori) Nenpòt Nenpòt Okenn (tankou-soude) Pa disponib 316L
Ba klori<200 <80 450°C, 1 hour Forced air 316 
Modere klori 200-500<80 450°C, 1 hour Forced air or water quench Preferred 316L
Segondè klori 500-1500<70 450°C, 1 hour Water quench 316L necessary
Very high chloride >1500 <60 500-550oC, 1 hour Water quench 316L (or upgrade to duplex)
Efikasite PWHT sou Verifikasyon Field

Pou aparèy chofaj nan-sèvis, kote istwa PWHT a pa konnen, yo ka itilize de metòd pou detèmine si estrès rezidyèl yo te libere ase. Premye a se tès koube ASTM G38 U-, kote yon ti echantiyon ki soti nan pati dwat aparèy chofaj la koube 180 degre epi mete l nan klori mayezyòm bouyi. Si fann devlope anvan 100 èdtan, estrès rezidyèl yo depase 100 MPa. Dezyèm fason an se pou mezire estrès rezidyèl nan soude a pa difraksyon reyon X-men sa mande ekipman espesifik. Sa a se solisyon reyalis pou pifò kliyan yo. Mete espesifikasyon PWHT sou lòd acha a epi chèche verifye si pwosedi a (tan, tanperati, metòd refwadisman) te swiv.

Konklizyon: Spesifikasyon to refwadisman kòm yon pati nan PWHT pou sèvis klori

Pou 316 bouchon fen aparèy chofaj asye pur, apre -tretman chalè soude nan 450 degre pou 1 èdtan ki te swiv pa refwadisman lè fòse bay 80-85% soulajman estrès san sansibilizasyon, anpil amelyore rezistans nan SCC ak pitting nan anviwònman klori. Li pa rekòmande pou ralanti fre (nan yon gwo founo dife) paske sa a ta diminye efikasite nan soulajman estrès. Trempe dlo bay maksimòm rediksyon estrès, men tou ogmante konpleksite ak risk . 316L yo ta dwe espesifye ak trempe dlo yo mande pou PWHT nan tanperati ki pi wo (500-600 degre) pou anpeche sansibilizasyon. Pou sèvis klori, enjenyè ki espesifye PWHT dwe defini tou tanperati kenbe ak metòd refwadisman. Metodoloji yo bay isit la pèmèt kliyan yo chwazi paramèt PWHT ki maksimize rezistans korozyon pandan y ap anpeche sansibilizasyon endezirab ki ta ka rive ak refwadisman ki pa apwopriye, lè yo asosye pousantaj refwadisman ak estrès rezidyèl ak rezistans pitting.